동전해정제시 음극분극전위에 미치는 첨가제의 영향에 관한 연구

Abstract

전해첨가제를 동전해액(황산동-황산)에 각각 단독으로 ?풔? 복합적으로 첨가하여 음극분극전위를 측정함으로써 다음과 같은 결론을 얻었다.

1) 첨가량이 많아짐에 따라 아교와 글리신은 음극분극전위를 현저히 높이며, 아비톤-A는 약간 증가시키고, 티오요소는 소량 첨가할 경우 감소시키나 첨가량이 많아지면 상당히 상승시킨다. 그리고 Cl?은 음극분극전위에 영향을 거의 미치지 않는다.

2) 아교를 주 첨가제로하고 티오요소 및 아비톤-A를 첨가했을 때 티오요소와 아비톤-A는 분극전위에 거의 영향을 미치지 못하고 주로 아교가 영향을 미친다.

3) 아교 5mg/l, 티오요소 3mg/1, Cl? 20mg/l를 가한 전해액을 이용한 일반적인 전해정제로 2.5A/dm²의 고전류밀도에서 평활하고 치밀한 전착면을 얻을 수 있었으며, 불순물의 제거가 가능하고 부동태현상이 발생 하지 않았다.

Cathodic polarization potentials during the ectrorefining of copper have been measured under various conditions of addition agents in the copper electrolyte (CuSO₄-H₂SO₄).

The results obtained are as follows.

1) The cathode polarization potential is affected by the kind of addition agents and the amount of addition to the electrolyte. Glue and glycine show remarkable increasing effects on the polarization potential, Aviton-A has a little effect.

However, thiourea causes the polarization potential to increase considerably at high concentration, but showing a decreasing effect at low concentration.

Chlorine has little effect on the polarization potential.

2) In the case of using the electrolyte containing glue with Aviton-A and glue with thiourea as additives, thiourea and Aviton-A have little effect on the polarization potential, while glue shows remarkable effect.

3) The electrorefining was carried out successfully using the electrolyte added glue 5mg/l, thiourea 3mg/l, and chlorine 20,g/l, with the current thiourea 3mg/l, and chlorine 20mg/l, with the current density of 2.5A/dm² for 68hrs at the pilot plant. The surface of deposit copper was smooth and its thickness was uniform, showing the purity of 99.99( copper.

Cathodic polarization potentials during the ectrorefining of copper have been measured under various conditions of addition agents in the copper electrolyte (CuSO₄-H₂SO₄).

The results obtained are as follows.

1) The cathode polarization potential is affected by the kind of addition agents and the amount of addition to the electrolyte. Glue and glycine show remarkable increasing effects on the polarization potential, Aviton-A has a little effect.

However, thiourea causes the polarization potential to increase considerably at high concentration, but showing a decreasing effect at low concentration.

Chlorine has little effect on the polarization potential.

2) In the case of using the electrolyte containing glue with Aviton-A and glue with thiourea as additives, thiourea and Aviton-A have little effect on the polarization potential, while glue shows remarkable effect.

3) The electrorefining was carried out successfully using the electrolyte added glue 5mg/l, thiourea 3mg/l, and chlorine 20,g/l, with the current thiourea 3mg/l, and chlorine 20mg/l, with the current density of 2.5A/dm² for 68hrs at the pilot plant. The surface of deposit copper was smooth and its thickness was uniform, showing the purity of 99.99( copper.